Superhard dielectric compounds and methods of preparation

ABSTRACT

Novel superhard dielectric compounds useful as gate dielectrics discovered. Low temperature methods for making thin films of the compounds on substrate silicon are provided. The methods comprise the step of contacting a precursor having the formula H 3 X—O—XH 3 , wherein X is silicon or carbon with a compound comprising boron or nitrogen in a chemical vapor deposition (CVD) chamber or with one or more atomic elements in a molecular beam epitaxial deposition (MBE) chamber. These thin film constructs are useful as components of microelectronic devices, and specifically as gate dielectrics in CMOS devices.

CROSS REFERENCE

[0001] This application claims priority from U.S. Provisional Patent Application Serial No. 60/328,967 filed Oct. 11, 2001, the disclosure of which is incorporated by reference herein in its entirety.

STATEMENT OF GOVERNMENT FUNDING

[0002] The U.S. Government through the US Army Research Office provided financial assistance for this project under Grant No. DAAD19-00-1-0471 and through the National Science Foundation under Grant No. DMR-9986271, Grant No. DMR 9902417 and Grant No. ECS 0000121. Therefore, the United States Government may own certain rights to this invention.

FIELD OF INVENTION

[0003] This invention relates generally to certain super-hard dielectric compounds useful as gate dielectrics in microelectronic devices. Low temperature methods for depositing thin films of these compounds onto silicon substrates are presented.

BACKGROUND

[0004] Recently, the challenge of creating smaller dimensions in microelectronic devices has demanded the use of new materials for the gate dielectric—either thinner silicon oxide layers or new compounds having a higher dielectric constant.

[0005] Silicon dioxide (SiO₂) is a classical refractory material and the most common gate dielectric in microelectronic devices. Its structure is made up of SiO₂ tetrahedra in which each oxygen forms two bonds with neighboring Si atoms ((SiO₄)⁻⁴ tetrahedra connected through bridging oxygens). The performance of SiO₂-containing devices is limited by dopant diffusion out of poly-Si and direct tunneling through SiO₂, and when off-state, power dissipation becomes comparable to active power.

[0006] Current efforts are focused on replacing SiO₂ with nitride (Si₃N₄) or oxynitride (SiOxNy) films with K ˜5-7.5 [1-6] or with alternative higher K (˜20-30) films [7,8]. In recent years, nitride oxides (silicon oxynitrides) have been widely investigated as possible substitutes for SiO₂ because of their higher stability and durability, their ability to prevent boron diffusion, and their higher dielectric constant. The introduction of three-coordinate nitrogen into SiO₂ increases the cross-linking in the structure, resulting in a compound having higher density, strength, and hardness in comparison to the pure silicon oxide. Compounds in the Si—O—N system exhibit good thermal, chemical, and mechanical stability, as well as diffusive barrier and dielectric properties [9]. In addition, Si₂N₂O has superior oxidation resistance and thermal shock resistance compared to Si₃N₄. Most of the reported Si—O—N systems are amorphous and appear to have a higher dielectric constant than the pure oxide.

[0007] However, crystalline materials with well-defined compositions and structures have been sought which will give significant improvements in mechanical and electrical properties over more amorphous forms of these compounds. The synthesis of phases with well-defined composition and structure is desirable because it may lead to significant improvements and/or controllability in the mechanical, electrical, and dielectric properties [10, 11].

[0008] One such phase is stoichiometric, silicon oxynitride (Si₂N₂O), a refractory material having all the aforementioned and desirable properties. Si₂N₂O has the high-pressure B₂O₃ structure [12] and is composed of SiN₃O tetrahedral, corner-linked by O and N atoms. This structure is illustrated in FIG. 2. In this structure, the oxygen bridges two Si (as in SiO₂) and the N and Si atoms are, respectively, in three and four fold coordination as in Si₃N₄ [13].

[0009] The synthesis of this compound and the search for related silicon-based dielectric materials has been the focus of intense research because of their potential for enhanced performance compared to SiO₂ and Si₃N₄ based devices [14,15]. However, despite their attractive properties, a suitable synthesis technique for silicon oxynitrides and related dielectrics at relatively low processing temperatures, as required in silicon device technology, is still lacking.

IN THE DRAWINGS

[0010]FIG. 1 is a ball-and-stick model illustrating the unit cell structure of Si₂B₂O.

[0011]FIG. 2 is a ball-and-stick model illustrating the structure of Si₂N₂O

[0012]FIG. 3 is a Rutherford Back Scattering (RBS) spectrum of a Si₂N₂O film deposited at 850° C. The RBS simulation by RUMP, shown as a dashed line, gives the atomic compositions of Si, O, and N.

[0013]FIG. 4 illustrates the L_(2,3) ionization edge of Si and the K ionization edges of O and N (inset) in an EELS spectrum of Si₂N₂O.

[0014]FIG. 5 is a SIMS elemental depth profile of Si₂N₂O showing a uniform distribution of the elements.

[0015]FIG. 6 is a FTIR spectrum of a Si₂N₂O showing the N—Si—O absorption peaks corresponding to stretching (900 cm⁻¹) and bending (470 cm⁻¹) modes.

[0016]FIG. 7 is AFM image of the Si2B2O film surface showing relatively flat morphology and an array of indentations used to determine the microhardness. Inset is an enlarged view of typical nanoindentation

SUMMARY

[0017] Novel superhard dielectric compounds useful as gate dielectrics in microelectronic devices have been discovered. Low temperature methods for making thin films of the compounds on substrate silicon are provided. The methods comprise the step of contacting a precursor having the formula H₃X—O—XH₃, wherein X is silicon or carbon with a compound comprising boron or nitrogen in a chemical vapor deposition (CVD) chamber or with one or more atomic elements in a molecular beam epitaxial deposition (MBE) chamber. These thin film constructs are useful as components of microelectronic devices, and specifically as gate dielectrics in CMOS devices.

[0018] Compounds having a formulae XqYpZtO wherein X is silicon or carbon, Y is boron or nitrogen, Z is gallium or aluminum, O is oxygen and q and p are each an integer having a value of 1,2 or 3 and t is zero or 1, provided that when X is silicon, and t is zero, Y is not nitrogen are presented. Also presented are non-stoichiometric compounds having the formulae XqYpZtO wherein X is silicon or carbon, Y is boron or nitrogen, Z is gallium or aluminum, O is oxygen wherein one or more of the values of q, p or t are non-integral.

[0019] In certain preferred embodiments of the invention the compounds have a dielectric constant between 3 and 7, most preferably between about 5.5 and 6.6.

[0020] In certain other preferred embodiments the compounds have a hardness of between about 17 to 25 GPa.

[0021] In one preferred embodiment of the present invention X is Si and Y is boron and most

[0022] preferably have the formula Si₂B₂O or SiB₂O.

[0023] In other preferred embodiments of the present invention, X is carbon and Y is boron and most preferably has the formula C₂B₂O.

[0024] In other preferred embodiments X is silicon, Y is nitrogen and Z is aluminum, most preferably the compound having the formula Si₂N₃AlO.

[0025] Most preferably the non-stoichiometric compounds of the present invention are silicoxynitrides wherein X is silicon, Y is nitrogen and the values of q, p and t are non-integral.

[0026] In an important aspect of the present invention, the compounds are provided as thin films deposited on a silicon substrate. Preferably thin films of the compounds of the present invention have a thickness of between about 5 and 500 nm Most preferably the silicon substrate, a silicon wafer, e.g., is Si(100), Si(111) or doped Si(111) as generally utilized as semiconductor devices. In certain preferred embodiments, the silicon substrate comprises a native oxide layer. In other preferred embodiments, the silicon substrate is cleaned prior to deposition of film In yet other preferred embodiments the silicon substrate comprises compliant buffer layers Substrates other than silicon generally employed in semiconductor devices may likewise be utilized.

[0027] In an important aspect of the present invention, microelectronic devices comprising the present thin film of any of the compounds of the present invention deposited on a suitable substrate are provided. Because of their dielectric and other physical properties, thin films of the compounds of the present invention are useful gate dielectrics in microelectronic devices CMOS, e.g., and may be incorporated into semiconductor devices generally as substrates for other components of integrated circuits by methods known in the art.

[0028] In another important aspect of the invention, low temperature methods for preparing thin film of the present superhard dielectric compounds are provided. These low-temperature methods are compatible with current silicon processing technologies. Methods are provided for preparing thin films of compounds having a formulae XqYpZtO wherein X is silicon or carbon, Y is boron or nitrogen, Z is gallium or aluminum, O is oxygen and q and p are each an integer having a value of 1, 2 or 3 and t is zero or 1 comprising the step of contacting precursor having the formula H₃X—O—XH₃ with a reactive species containing Y or Z in the presence of substrate under conditions whereby thin film of the compound is deposited on the substrate. Methods are provided for contacting the precursor and reactive species in a chemical vapor deposition (CVD) chamber or a molecular beam epitaxial (MBE) chamber. The thin films prepared by the methods generally have a thickness between about 5 and 500 nm Preferably, the substrate is Si(100), Si(111) or doped Si(111). Other substrates known to the art and used as substrate in preparation of thin film devices may also be employed. In certain preferred embodiments of the invention, the substrate comprises a native oxide layer. In certain other preferred embodiments, the substrate is cleaned prior to deposition of thin film compounds. In yet other preferred embodiments the substrate may comprise a compliant buffer layer.

[0029] In certain preferred embodiments of the method of the present invention, methods are presented for preparing a compound having the formula XqYpO wherein X is silicon, Y is boron, O is oxygen and q and p are each an integer having a value of 1 or 2, comprising the step of contacting a precursor having the formula H₃X—O—XH₃ with a reactive compound having the formula (YL₃)_(v) wherein L is hydrogen or halide and v is 1 or 2 in the presence of substrate in a chemical vapor deposition chamber under conditions whereby thin film of said compound is deposited on said substrate. Thin films made by this preferred method are presented. Microelectronic devices comprising the deposited thin films are presented.

[0030] In a preferred embodiment of this method, low temperature methods for depositing superhard dielectric thin films of Si₂B₂O on a silicon substrate are presented. In these embodiments, essentially equimolar amounts of precursor H₃SiOSiH₃ and (BH₃)₂ are contacted in a CVD chamber at a temperature at about 700° C. to 1000° C., most preferably about 700° C., in the presence of the silicon substrate under conditions whereby the H₃SiOSiH₃ and B₂H₆ react to form thin film of Si₂B₂O on the silicon substrate. In these preferred embodiments, films of Si₂B₂O having a thickness of about 5 to 500 nm may be formed on silicon substrate, Si(100) or Si(111) or doped Si(111), for example. The substrate may comprise a native oxide layer, or may be cleaned before the deposition of film Thin film of Si₂B₂O on a silicon substrate thin film of Si₂B₂O are provided.

[0031] In another preferred embodiment, low temperature methods for depositing superhard dielectric thin films of SiB₂O on a silicon substrate are presented. In these embodiments, equimolar amounts of precursor H₃SiOSiH₃ and (BH₃)₂ are contacted in a CVD chamber at a temperature between about 500-650° C. in the presence of the silicon substrate under conditions whereby the H₃SiOSiH₃ and B₂H₆ react to form thin film of Si₂B₂O on the silicon substrate. In these preferred embodiments, films of SiB₂O having a thickness of about 5 to 500 nm may be formed on silicon substrate, Si(100) or Si(111) or doped Si(111), for example. The substrate may comprise a native oxide layer or may be cleaned before the deposition of film 34. Thin film of SiB₂O on a silicon substrate is provided.

[0032] In an important aspect of the invention, microelectronic devices comprising thin film of silicoxyborides, most specifically SiB₂O or Si₂B₂O are given.

[0033] In yet another preferred embodiment, low temperature methods for depositing superhard dielectric thin films of Si₂N₂O on a silicon substrate are presented. In these preferred embodiments, essentially equimolar amounts of precursor H₃SiOSiH₃ and NH₃ are contacted in a CVD chamber at a temperature between about 650° C. to 850° C. in the presence of the silicon substrate under conditions whereby the H₃SiOSiH₃ and NH₃ react to form thin film of Si₂N₂O on the silicon substrate. In this preferred method, thin film of Si₂N₂O having a thickness of about 5 to 500 nm may be formed on a silicon substrate, Si(100) or Si(111) or doped Si(111), for example. The substrate may comprise a native oxide layer or may be cleaned prior to deposition of film. Thin film of Si₂N₂O on a silicon substrate prepared by these methods are given.

[0034] In another important aspect of the invention microelectronic devices comprising thin film of Si₂N₂O made by the methods of the present invention are presented.

[0035] In yet another preferred embodiment of the present invention, methods for depositing superhard thin films of B₂C₂O on a silicon substrate are presented. In these preferred methods, essentially equimolar amounts of H₃COCH₃ and BCl₃ are contacted in said chamber at a temperature between about 650° C. to 850° C. in the presence of the silicon substrate under conditions whereby the H₃COCH₃ and BCl₃ react to form thin film of B₂C₂O on the silicon substrate. B₂C₂O films formed by these methods may have a thickness of about 5 to 500 nm The substrate is preferably silicon, Si(100) or Si(111) or doped Si(111), for example. The substrate may comprise a native oxide layer or may be cleaned prior to deposition of film Thin film of B₂C₂O on silicon substrate are provided.

[0036] In yet another important aspect of the invention, microelectronic devices comprising thin film of borocarboxyoxides, specifically thin film B₂C₂O are given.

[0037] In another preferred embodiment of the method of the present invention, methods are presented for preparing thin film of a compound of the present invention having a formula XqYpZtO wherein X is silicon or carbon, Y is boron or nitrogen, Z is gallium or aluminum, O is oxygen and q and p are each an integer having a value of 1, 2 or 3 and t is zero or 1 and for preparing non-stoichiometric compounds XqYpZtO wherein one or more of the values of q, p or t are non-integral. The method comprises the step of directing Y atoms at a precursor having the formula H₃X—O—XH₃ in a molecular beam epitaxial chamber in the presence of a silicon substrate under conditions whereby the precursor and Y atoms combine to form thin film on the substrate. Preferably the substrate is Si(100), Si(111) or doped Si(111) and may comprise a native oxide layer or be cleaned by methods known in the art prior to deposition. Thin film of these compounds on a silicon substrate are provided. Substrates other than silicon known to the art may also be employed as substrate.

[0038] In another important aspect of the invention, microelectronic devices comprising thin film of a compound made by these methods are provided.

[0039] In preferred embodiments of the method of this present invention, superhard thin films of non-stoichiometric siliconoxynitrides are prepared. In this preferred method, atomic nitrogen generated in a molecular beam deposition chamber is directed at precursor H₃SiOSiH₃ in the presence of silicon substrate under conditions whereby the precursor and nitrogen atoms react to form thin film of non-stoichiometric silicon oxynitrides on the silicon substrate. Preferably the temperature of the chamber is about 850° C. to 950° C. The substrate may be Si(100), Si(111), doped Si(111) or other substrate known to the art and may comprise a native oxide layer, compliant buffer or may be cleaned prior to deposition of the thin film Preferably the temperature of said chamber is between about 850 to 950° C. and the substrates is highly doped Si(111). Thin film of non-stoichiometric silicoxynitrides deposited on a silicon substrate by these methods are provided.

[0040] In yet another important aspect of the invention, microelectronic devices comprising a thin film of non-stoichiometric silicoxynitride made by the present methods are provided.

[0041] In certain preferred instances of the invention, methods for depositing superhard thin films of Si₂N₃AlO on a silicon substrate are given. In these methods atomic nitrogen and atomic aluminum are directed at precursor is H₃SiOSiH₃ in a molecular beam deposition chamber in the presence of a silicon substrate under conditions whereby the disiloxane reacts with nitrogen atoms and aluminum atoms to form thin film of Si₂N₃AlO on the silicon substrate. In these instances, the silicon substrate may comprise compliant buffer layers comprising in situ generated SiAlONS and related Al silicon oxynitrides. Thin film of Si₂N₃AlO on a silicon substrate are provided.

[0042] In yet another important aspect of the present invention, microelectronic devices comprising thin film of Si₂N₃AlO are provided.

[0043] In an important aspect of the invention, compounds having the formula H₃XOXH₃ wherein X is silicon or carbon are presented as precursors in the preparation of the compounds of the present invention. In preferred instances, H₃SiOSiH₃ is presented as a precursor in the preparation of the compounds of the silicon-based compounds of the present invention. In other preferred instances, H₃COCH₃ is presented as a precursor in the preparation of the compounds of the carbon-based compounds of the present invention.

[0044] In an important aspect of the present invention, methods are provided for preparing disiloxane having the formula H₃SiOSiH₃ The method comprises the steps of contacting a halosiloxane, preferably Cl₃SiOSiCl₃, with a salt of gallium tetrahydride, preferably LiGaH₄, and capturing gaseous H₃SiOSiH₃ generated during the reaction between halosiloxane and the hydride. Disiloxane prepared by this method may be used as a precursor for the preparation of thin films of the compounds of the present invention. Preferred compounds made from siloxane prepared by the method of the present invention are Si₂N₂O, non-stoichiometric siloxynitrides, silicoborohydrides, most preferably SiB₂O and Si₂B₂O, and Si₂N₃AlO.

[0045] In yet another aspect of the compounds of the present invention may be used as superhard coatings in a variety of applications.

DETAILS OF THE INVENTION

[0046] While the present invention will be described more fully hereinafter with reference to the examples and accompanying drawings, in which aspects of the preferred manner of practicing the present invention are shown, it is to be understood at the outset of the description which follows that persons of skill in the appropriate arts may modify the invention herein described while still achieving the favorable results of this invention Accordingly, the description which follows is to be understood as being a broad, teaching disclosure directed to persons of skill in the appropriate arts, and not as limiting upon the present invention.

[0047] This invention provides novel superhard compounds having dielectric constants that make them useful as gate dielectrics in CMOS devices and as superhard coatings in a variety of applications. In certain preferred instances, the compounds comprise a Si—O backbone structure and a light element boron or nitrogen. In other instances the compounds comprise a C—O backbone structure and a light element, boron or nitrogen. Compounds having the Si—O backbone and nitrogen and aluminum are also provided.

[0048] Generally, the crystalline structures of these compounds are compact which gives them their hardness and electronic properties. Preferred compounds Si₂B₂O and SiB₂O, for example, are isoelectronic to carbon (i.e., four valence electrons per atom) and they crystallize with highly dense diamond-like structures in which all the constituent elements are tetrahedrally coordinated. This leads to superior properties such as superhardness and high stability at extreme conditions. In fact, such materials may be alternatives to diamond in high performance applications. Si₂B₂O has a structure that consists of SiB₂O tetrahedra linked at their corners by O and B atoms. This is essentially the Si₂N₂O structure with all the N atoms at the trigonal sites replaced by sp² hybridized B (FIG. 1). Alternate structure related to diamond that is denser and harder may also be possible. In this structure all the elements occupy exclusively tetrahedral sites as in diamond. This structure is feasible since SiB₂O is isoelectronic to diamond and is in essence a stoichiometric hybrid between Si and B₂O. The latter is a highly sought binary phase of boron with 3-D diamond-like structure that has been predicted to have extreme hardness and other important electronic and mechanical properties.

[0049] C₂B₂O is the carbon analogue of Si₂B₂O. This system is a stoichiometric hybrid between diamond and the superhard phase B₂O phase. C₂B₂O in the diamond cubic structure but has superior properties such as superhardness as well as higher resistance to oxidation and higher thermal stability than diamond. Si₂N₂O another preferred embodiment has the high pressure B₂O₃ structure and it is composed of SiN₃O tetrahedra linked at their corners by O and N atoms (FIG. 2). Each oxygen is connected to two Si (as in SiO2) and the N and Si atoms are, respectively, three and four fold coordinate as in Si3N4.

[0050] Certain preferred compounds of the present invention are silicon-based oxygen and boron-containing compounds having the formula Si_(a)B_(b)O_(d), most preferably Si₂B₂O or SiB₂O. Other preferred compounds are, non-stoichiometric silicon-based oxygen and nitrogen-containing compounds, siliconoxynitrides having the formula Si_(a)N_(b)O. In yet other preferred embodiments carbon-based compounds having the formula C_(a)B_(b)O, most preferably C₂B₂O are provided. In certain other preferred embodiments of the present invention, compounds having the formula Si_(a)N_(b)Z_(c)O_(d) wherein Z is aluminum is provided. Most preferably the compound has the formula Si₂N₃AlO.

[0051] A highly practical and a low-temperature chemical vapor deposition (CVD) method, involving an entirely new approach based on a stoichiometric heterogeneous reaction from gaseous reactants, is described for depositing Si₂N₂O films (5-500 nm) on Si substrates. A new and practical method for depositing superhard thin films of refractory and dielectric silicon oxynitrides, via CVD and MBE reactions of the molecular precursor H₃Si—O—SiH₃, is demonstrated. Specifically, stoichiometric Si₂N₂O and non-stoichiometric SiO_(x)N_(y) films were deposited on Si substrates at 600-850° C., and characterized for their phase, composition, and structure by RBS, EELS, FTIR, FESEM, and HRTEM. The leakage current density voltage (J_(L)-V) characteristics and the capacitance-voltage (C-V) as a function of frequency were determined on MOS (Al/Si₂N₂O/SiO/p-Si) structures. The leakage current density, J_(L) at −6V (+6V) for a 20 nm Si₂N₂O film was 0.1 nA/cm² (0.05 nA/cm²). The dielectric permittivity, K, estimated from the capacitance density in accumulation, was 6 and frequency dispersionless. From the negative flat ban shift (ΔV_(fb)) of 150 mV, the positive fixed charge density (N_(f)) at the Si(100)/SiO interface was calculated to be 2.3×10¹¹/cm³. The microhardness of Si₂N₂O was determined to be 18 GPa.

[0052] The key aspect of this deposition technique is the use of a completely inorganic source (H₃Si—O—SiH₃) that incorporates the crucial Si—O—Si building block of the target solids, and which does not possess the typical impurity elements such as Cl and C that are potentially detrimental to the electrical and dielectric properties of the material. Moreover, its stoichiometric reaction with NH₃ leads to the complete elimination of its H ligands to yield high purity Si—O—N films. This precursor compound also offers an ideal synthetic route for the formation of technologically important oxynitrides, with controlled stoichiometries, and at low temperatures compatible with silicon processing technology.

[0053] A novel low-temperature (600-850° C.) chemical vapor deposition (CVD) method, involving the reaction between disiloxane (H₃Si—O—SiH₃) and ammonia (NH₃) is presented to deposit stoichiometric, Si₂N₂O, and non-stoichiometric, SiO_(x)N_(y), silicon oxynitride films (5-500 nm) on Si substrates. The gaseous reactants are free from carbon and other undesirable contaminants. The deposition of Si₂N₂O on Si [with (100) orientation and a native oxide layer of 1 nm] was conducted at a pressure of 2 Torr and at extremely high rates of 20-30 nm per minute with complete hydrogen elimination.

[0054] The deposition rate of SiO_(x)N_(y) on highly-doped Si [with (111) orientation but without native oxide] at 10⁻⁵ Torr was ˜1.5 nm per minute, and achieved via the reaction of disiloxane with N atoms, generated by an RF source in an MBE chamber. The phase, composition and structure of the oxynitride films were characterized by a variety of analytical techniques. The hardness of Si₂N₂O, and the capacitance-voltage (C-V) as a function of frequency and leakage current density-voltage (J_(L)-V) characteristics were determined on MOS (Al/Si₂N₂O/SiO/p-Si) structures. The hardness, frequency-dispersionless dielectric permittivity (K), and J_(L) at 6V for a 20 nm Si₂N₂O film were determined to be 18 GPa, 6, and 0.05-0.1 nA/cm³, respectively.

[0055] Additionally, the deposition of non-stoichiometric SiO_(x)N_(y) is also demonstrated. The films are characterized by Rutherford backscattering spectroscopy (RBS), secondary ion mass spectrometry (SIMS), high-resolution transmission electron microscopy (HRTEM) and spatially-resolved electron energy loss spectroscopy (EELS), Fourier transform infrared spectroscopy (FTIR), field-emission scanning electron microscopy (FESEM), a Triboscope attached to an atomic force microscope (AFM) for hardness, and electrical and dielectric methods.

[0056] The synthetic reaction is similar to that for Si₂N₂O and is illustrated by the equation (1):

H₃SiOSiH₃+B₂H₆→H₂+Si₂B₂O   (1)

[0057] Also presented are methods for preparing the carbon analogs of the silicon-based compounds utilizing the precursor dimethyl ether, H₃COCH₃ in the CVD or MBE chamber. Compounds made by these methods are, for example, C₂B₂O.

[0058] The thin films are characterized by Rutherford backscattering spectroscopy (RBS), secondary ion mass spectrometry (SIMS), high-resolution transmission electron microscopy (HRTEM) and spatially-resolved electron energy loss spectroscopy (EELS), Fourier transform infrared spectroscopy (FTIR), field-emission scanning electron microscopy (FESEM), a Triboscope attached to an atomic force microscope (AFM) for hardness, and electrical and dielectric methods.

[0059] Determination of the hardness of the compounds give values of GPa of between about 17 to 25 Gpa. These values illustrate the usefulness of the compounds as superhard coatings in a variety of applications. FIG. 7 is AFM image of the preferred embodiment Si2B2O film surface showing relatively flat morphology and an array of indentations used to determine the microhardness. Inset is an enlarged view of typical nanoindentation

[0060] Chemical Precursors

[0061] Disiloxane

[0062] The key feature in the method for deposition of thin films of the present invention comprising silicon is the use of the simple disiloxane (H₃Si—O—SiH₃) precursor [16]. The major advantage of utilizing H₃Si—O—SiH₃ is the presence of the Si—O—Si framework in the molecule, which provides both the building block for the desired 3-D network and essentially fixes the necessary Si to O ratio. Additionally, the H₃Si—O—SiH₃ compound is stable and volatile with a boiling point of —15° C. The vapor pressure at −82° C., 145° C. and −23° C. are 15, 195 and 563 Torr, respectively [16]. The precursor can be stored almost indefinitely in stainless steel containers and like most silanes, ignites spontaneously but not explosively upon contact with air. Moreover, it does not contain carbon or any other potentially impure elements (e.g., Cl, F) in the molecular structure. The deposition of Si₂N₂O films is illustrated in the following reaction (2):

H₃Si—O—SiH₃+NH₃→6H₂+Si₂N₂O   (2)

[0063] Moreover, the use of active N species in place of NH₃, with controlled energies, may also be used to tailor the N to O ratio in a desired material. Therefore, non-stoichiometric films (SiO_(x)N_(y)), with composition and property intermediate to those of stoichiometric Si₃N₄ and stoichiometric SiO₂, may be readily engineered.

[0064] Disiloxane is commercially available and also may be prepared by methods disclosed in the present invention.

[0065] Dimethyl Ether

[0066] The deposition of thin films of the present invention comprising carbon proceeds through the use of the dimethyl ether precursor. Dimethyl ether is commercially available. The simple dimethyl ether precursor may be used in either the CVD chamber or the MBE chamber to make the carbon analogues of the compounds of the present invention. Carbon analogues of the silicon compounds have similar hardness and dielectric properties

[0067] The deposition of B₂C₂O films is illustrated in the following reaction (3):

H₃C—O—CH₃+BCl₃→B₂C₂O+6HCl   (3)

EXPERIMENTAL SECTION EXAMPLE 1

[0068] This example illustrates the deposition of Si₂N₂O films on silicon substrate in a chemical vapor deposition (CVD) chamber using siloxane as precursor.

[0069] The deposition of Si₂N₂O films was carried out in a CVD reactor consisting of a cold-wall quartz tube fitted with a recirculating jacket. The reactor wall temperature was maintained at 700° C. by recirculating preheated ethylene glycol. The Si substrate was p-Si wafer having resistivity of 4.5×10-3 ohm/cm. The substrates were inductively heated using a high-grade, single-wafer graphite susceptor. Prior to its initial use, the susceptor was out-gassed at 1100° C. under high vacuum (10⁻³ Torr), and then coated with Si via SiH₄ decomposition. The pumping system was comprised of a high capacity turbo-molecular pump and a corrosion-resistant pump. The former was used to obtain high vacuum before and after each deposition, and the latter was used during deposition. A typical reactor base pressure was 5-6×10⁻⁷ Torr. The gaseous reactants, H₃Si—O—SiH₃ and NH₃, were diluted with research grade N₂ and introduced into the reactor through precalibrated glass flow controllers. The deposition was conducted at a pressure of 2 Torr and temperatures between 600-850° C. Under these conditions, stoichiometric Si₂N₂O films ranging in thickness between 5 and 500 nm, were deposited on Si [with an orientation of (100) and a native oxide layer of 1 nm] at extremely high rates of 20-30 nm per minute.

[0070] Physico-Chemical Characterization of Si₂N₂O Films Prepared in Example 1

[0071] RBS in the random mode was routinely used to obtain the Si, N, and O concentration and to estimate the film thickness. A typical plot is illustrated in FIG. 2. Additionally, elastic N and O resonance nuclear reactions at 3.72 MeV and 3.0 MeV, respectively, were used to establish the precise Si₂N₂O elemental ratios. Since forward recoil experiments indicated that the hydrogen content was at background levels, the elimination of the Si—H and N—H bonds from the reactants occurred completely during growth.

[0072] SIMS was used to confirm the presence of the desired elements and the absence of carbon impurities, and to demonstrate that the elemental content was homogeneous throughout the material. A representative SIMS depth profile, showing the highly uniform elemental distribution in the film thickness direction, is given in FIG. 5.

[0073] HRTEM (not shown here) indicated that the films were highly uniform in thickness and displayed flat and smooth surface morphology. The selected area electron diffraction (SAED) and high-resolution images confirmed that the material was amorphous. Spatially-resolved EELS, used to examine the elemental content at the nanometer scale and characterize the local bonding environment of the atoms, showed that the constituent elements appeared at every nanometer step probed; this consistent with a single-phase material. The absolute elemental concentration (determined by EELS) was close to the stoichiometric value for Si₂N₂O, which corroborated the RBS results. An EELS spectrum featuring the ionization edges of the elements is shown in FIG. 4. The near-edge fine structure is indicative of a 3-D Si₂N₂O network.

[0074] The FITR spectrum in FIG. 6 exhibited phonon modes consistent with the single-phase Si₂N₂O. A strong, well-defined peak centered at 900 cm−1 and a weak peak at 470 cm−1 corresponds to the N—Si—O stretching and bending modes, respectively, of the Si₂N₂O phase [15]. Note, the 900 cm−1 peak is located at frequencies intermediate to those of the corresponding stretching odes for stoichiometric SiO₂ (˜980 cm−1) and Si₃N₄ (˜850 cm−1). Moreover, in the region between 2100 cm−1 and 2000 cm−1, of the spectrum, additional peaks attributable to Si—H vibrations are absent. This is consistent with the RBS result of complete elimination of H ligands from the precursor.

[0075] The hardness of the films was determined using a Hysitron Triboscope attached to a Nanoscope III AFM (digital instruments). The hardness is defined as the applied load divided by the surface area of the impression when a pyramidal shaped diamond indentor is pressed normalloyinto the film. Pure quartz (SiO2) was used as a standard and its hardness was measured to be close to 9.5 GPa For example, the hardness of single-crystal Al2O3 (sapphire) was measured to be 22 GPa. Using the same experimental conditions, the hardness of the Si2N2O films are was approximately 18 GPa.

[0076] Characterization of Electrical and Dielectric Properties of Si₂N₂O Films Prepared in Example 1.

[0077] Including the native oxide layer (SiO₂; x˜1) of 1 nm [8], the observed Si₂N₂O film thicknesses by FESEM were 20 nm, 30 nm, 37.5 nm, and 65 nm, in agreement with RBS and HRTEM results. From the four-point probe measurement of the electrical resistivity of the Si wafer, the dopant density was estimated to be 2.5×10¹⁹ cm⁻³ [16]. For the room temperature electrical and dielectric measurements, aluminum (Al) top electrodes (100 nm thick and 530 um diameter) were deposited onto samples through a shadow mask by e-beam evaporation. Also, 100 nm Al films were deposited on the backside of Si to improve the bottom contacts. The samples were placed in an analytical probe system equipped with a chuck (3190 MC Systems), and the top electrodes were contacted with microprobes (1097 MODEL; mc Systems). The high frequency (1-100 KHz, ac_(osc) 20 mV ) capacitance-voltage (C-V) characteristics and the dc current-voltage (I-V) characteristics of the capacitors were measured using a multi-frequency LCR meter (HR Impedance analyzer, 4284A) and current meter (HPn4140B), respectively.

[0078] The leakage current densities, J_(t)(with 10 s delay), at −6V (−10V) and +6 V (+10V) for a 20 nm Si₂N₂O film were 0.1 nA/cm³ (100 nA/cm³) and 0.05 nA/cm3 (3nA/cm³), respectively. This asymmetry in the magnitude of J_(L) for positive and negative gate voltages stems from the asymmetry if the band alignment and band bending at the Si/SiO_(x) and Al/Si₂N₂O interfaces, and the consequent asymmetry in the transmission probability [19-22].

[0079] The C-V measurements were carried out on MOS (Al/Si₂N₂O/SiO/p-Si) structures. From the measured capacitance densities in accumulation (C_(acc)/A) at −5V, which were dispersionless in the frequency range measured, the total equivalent SiO₂ thickness or EOT_(tot)(i.e., EOT_(tot)=ε₀K_(SiO2)/(C_(acc)/A)) and K_(Si2N2O) as a function of Si₂N₂O thickness were calculated and are tabulated in Table I. Note, for these calculations the K of the interfacial SiO layer was estimated to be 7.8 (assuming a linear extrapolation between the K of 11.7 for Si and 3.9 for SiO₂) and quantum corrections were not applied.

[0080] From the slope of a Schotzky plot (1/C² versus V), with data from the depletion region (+1 to +5V) of the C-V curve for a 20 nm film at 100 KHz, the dopant density was calculated using the following equation [19] (4): $\begin{matrix} {N_{A} = {\frac{2}{{qK}_{s}A^{2}{{\left( {1/C^{2}} \right)}/{V}}} = {2.8 \times 10^{19}\quad {cm}^{- 3}}}} & (4) \end{matrix}$

[0081] where K_(s)=11.7, A=0.0022 cm² and (1/C²)/dV=9.7×10¹⁶. Note, this value of N_(A) is in agreement with that derived from the four-point probe method.

[0082] Considering this doping level (2.8×10¹⁹/cm of p-Si, the work function of Al (4.2 eV), and the electron affinity of Si (4.05 eV), the ideal flat band, V_(fbo)=φ_(MS) was calculated to be −0.85 V. At 100 KHz, the actual V_(fb) for the Al/Si₂N₂O/SiO/p-Si structure was −1V. This corresponds to a negative flat band shift (ΔV_(fb)=V_(fb)−φ_(MS) of) 150 mV. Therefore, the positive fixed charge density N_(f)=(ΔV_(fb)C_(acc))/qA) at the SiOSi interface was estimated to be 2.3×10¹¹/cm². The potential origin of this positive charge can be correlated with roughness at the Si(100)/SiO interface and the non-stoichiometry of SiO_(x)[19,21,23].

[0083] Table 1 gives the measured and estimated parameters, from C-V data at a frequency of 100 KHz, for Si₂N₂O film with different thickness. Note, φ_(MS)=−0.85 V, dopant density of p-Si is 2.8×10¹⁹/cm³, and electrode area=0.00216 cm². TABLE 1 Thickness of Si₂N₂O, nm t_(SiO), nm (C_(acc)/A), fF/μm² EOT_(tot), nm KSi₂N₂O 20 1 2.45 14.1 5.9 37.5 1 1.29 26.7 5.7 65 1 0.8 43.4 6.0

EXAMPLE 2

[0084] This Example illustrates the deposition of non-stoichiometric Si—O—N Films on Si substrated prepared MBE chamber utilizing siloxane as precursor.

[0085] The deposition of non-stoichiometric, silicon oxynitride (SiOxNy) films, via reactions of the H₃Si—O—SiH₃ precursor with N atoms generated by an RF source in an MBE chamber, was carried out. The base pressure of the chamber was 10⁻¹⁰ Torr, which increased to 10⁻⁴ Torr during the deposition. The plasma source power was operated at 400 W with a typical N pressure of 10⁻⁷ Torr. The SiO_(x)N_(y) films were deposited at 900° C. on highly-doped Si (111) substrates, which were previously flashed at 1050° C. and 10⁻¹⁰ Torr to remove the native oxide layer. The duration of each deposition was 30 to 45 minutes, yielding an average growth rate of ˜1.5 n per minute.

[0086] Characterization of Non-Stoichiometric Si—O—N Films Made by the Method of Example 2.

[0087] RBS analysis of these films illustrated inf FIG. 3 revealed that the Si, N and O concentrations were 45 at. %, 50 at.% and 5 at.%, respectively, indicating that the oxygen content in these films were substantially lower than that of Si₂N₂O (which is 20 at %). The FTIR spectrum showed the characteristic stretching mode at 845 cm⁻¹ which is lower in energy with respect to Si₂N₂O but almost identical to that of beta Si₃N₄. This data indicates that the bonding arrangement of this SiO_(x)N_(y) material is based predominately on the Si₃N₄ network with some of the lattice sites occupied by oxygen atoms. The dramatic deviation from the ideal Si₂N₂O stoichiometry is attributed to displacement of oxygen from the H₃Si—O—SiH₃ precursor by the highly reactive N atoms. Therefore, by judicious adjustments in the growth parameters, particularly the flux of the nitrogen beam, the O content in the films may be precisely tuned. Consequently this method provides a simple and convenient pathway leading to the formation of non-stoichiometric gate dielectric films with composition and properties intermediate to those of Si₃N₄ and SiO₂.

EXAMPLE 3

[0088] This example illustrates the deposition of C₂B₂O films on silicon substrate in a chemical vapor deposition (CVD) chamber using dimethylether as precursor.

[0089] The deposition of C₂B₂O films is carried out in a CVD reactor under the reaction conditions given in Example 1. The Si substrate is p-Si wafer. The gaseous reactants, CH3-O—CH₃ and BCl₃ are diluted with research grade N₂ and introduced into the reactor through pre-calibrated mass flow controllers. The molar ratio of BCl₃ to precursor is approximately 2:1. The deposition is conducted at a pressure of 2 Torr and temperatures between 600-850° C. Under these conditions, stoichiometric C₂B₂O films ranging in thickness between 5 and 500 nm, is deposited on Si.

EXAMPLE 4

[0090] This Example illustrates the deposition of Si₂B₂O films on silicon substrate in a chemical vapor deposition (CVD) chamber using disiloxane as precursor.

[0091] Thin films with composition close to the desired Si₂B₂O were deposited on Si(100) at 735° C. with rates ranging from 15 nm to 20 nm per minutes. An exactly stoichiometric mixture of the reactant gases and a deposition temperature above 700° C. were necessary to obtain films with Si₂B₂O stoichiometry.

EXAMPLE 5

[0092] This Example illustrates the deposition of SiB₂O films on silicon substrate in a chemical vapor deposition (CVD) chamber using disiloxane as precursor.

[0093] Thin films with composition close to SiB₂O were deposited on Si(100) under essentially same conditions as described in Example 4, but the temperature was lowered to 500 to 650° C. It is proposed that the Si deficiency in this relative to the Si2B2O compound prepared in Example 4 is due to incomplete reactions and possible elimination of SiH4 from the thermal disproportionation of the precursor as is illustrated in Equation (4):

H3Si—O—SiH3+B₂H₆ H₂+SiB₂O+SiH₄   (5)

[0094] Nevertheless, the SiB₂O composition in itself is unique because it is also isoelectronic to diamond and may crystallize with the diamond structure.

[0095] Characterization of Si₂B₂O and SiB₂O

[0096] The elemental concentrations of Si₂B₂O and SiB₂O were determined by RBS. SIMS was also used to confirm the presence of the desired elements and the lack of impurities, and to show that the elemental content was homogeneous through the material. FTIR showed bands corresponding to Si—O, B—O and Si—B lattice modes a result, consistent with the structure illustrated in FIG. 1. Cross-sectional TEM revealed that the as-deposited samples were amorphous. More crystalline samples may be prepared by reducing the growth rates and by conducting post-growth annealing. The hardness of Si₂B₂O was measured to be 17 GPa. The hardness of SiB₂O was measured to be 12 GPa

EXAMPLE 6

[0097] This Example illustrates the preparation of thin film Si₂AlN₃O in a MBE chamber. Precursor disiloxane was bombarded with nitrogen atoms and aluminum atoms in a MBE chamber under condition described in Example 2. The hardness of Si₂AlN₃O is 25 Gpa.

EXAMPLE 7

[0098] This Example illustrates the preparation of thin film B₂C₂O on a silicon substrate.

[0099] Precursor H₃COCH₃ and BCl₃ are contacted in essentially equimolar amounts in a CVD chamber according to the method described in Example 1. The chamber was maintained at a temperature of about 700° C. to 850° C. The thickness of the deposited B₂C₂O film was about 5 to 500 nm on Si(100) substrate. Si(111) and doped Si(111) may also be employed in this example and said substrate may comprise a native oxide layer or be cleaned by methods known in the art prior to deposition of B₂C₂O film.

EXAMPLE 8

[0100] This example illustrates the preparation of disiloxane H₃SiOSiH₃. Commercially available Cl₃SiOSiCl3 is diluted in diethyl ether and cooled to 78° C. Solid LiGaH4 is added to the Cl₃SiOSiCl3/solution through a solid addition funnel. Gaseous O(SiH3) is formed immediately and it is removed and purified by trap-to-trap distillation. The yield is typically 30-50%. The compound is identified by mass spectrometry and IR spectroscopy and shown to be identical with commercially available disiloxane.

[0101] Those skilled in the art will appreciate that numerous changes and modifications may be made to the preferred embodiments of the invention and that such changes and modifications may be made without departing from the spirit of the invention. It is therefore intended that the appended claims cover all such equivalent variations as fall within the true spirit and scope of the invention.

REFERENCES

[0102] [1] L. Feldman, E. P. Gusev, E. Garfunkel, in “Fundamental Aspects of Ultrathin Dielectrics on Si-based Devices”, Eds. E. Garfunkel, E. P. Gusev and Ya Vul'A, Kluwer, Dordrecht, Netherlands (1998).

[0103] [2] E. P. Gusev, H-C Lu, E. L. Garfunkel, T. Gustafsson, M. L. Green, IBM J. Res. Develop. 43, 265 (1999).

[0104] [3] S. V. Hattangady, H Niimi, G Lucovsky, J. Vac. Sci. Technol., A14, 3017 (1996).

[0105] [4] F. H. P. M. Habraken, A. E. T. Kuiper, Mater. Sci. Eng. Rep, R12, 123 (1994).

[0106] [5] G. Lucovsky, IBM J. Res. Dev, 43 301 (1999).

[0107] [6] Ultrathin SiO₂ and High-K Materials for ULSI Gate Dielectrics, Eds. H. Huff, C. A. Richter, M. L. Green, G. Lucovsky and T. Hattori, Materials Research Society, Warrendale, Pa. (1999).

[0108] [7] Alternative Gate Dielectrics for Microelectronics, Eds. R. W. Wallace and G. Wilk, MRS Bulletin, 27 [3] (2002).

[0109] [8] S. K Dey, C.-G. Wang, D. Tang, M. J. Kim, R. W. Carpenter, C. Werkhoven and E. Shero, submitted to Journal of Applied Physics, May 22, 2002.

[0110] [9] D. A. Buchanan. IBM J. Res. Develop, 43(3) (1999) 245.

[0111] [10] R. Roucka, J. Tolle, A. V. G Chizmeshya, P. A. Crozier, C. D. Poweleit, D. J. Smith, I. S. T. Tsong, and J. Kouvetakis, Phys. Rev. Lett., 88 (20) (2002) 206102.

[0112] [11] R. Roucka, J. Tolle, P. A. Crozier, D. J. Smith, I. S. T. Tsong, and J. Kouvetakis, Appl. Phys. Lett., 79 (2001) 2080.

[0113] [12] S. R. Srivinasa, L. Cartz, J. D. Jorgensen, T. G. Worlton R. A. Beyerlein, M. Billy, J. Appl. Cryst. 10 (1977) 167.

[0114] [13] I. Idrestedt, C. Brosset, Acta Chimica Scandinavica, 18 (1964) 1879.

[0115] [14] R. van Weeren, E. A. Leone, S. Curran, L. C. Klein, S. Danforth, J. Am. Ceram. Soc., 77 (1994) 2699.

[0116] [15] P. Wendor, R. de Ruiter, J. Chem. Soc. Chem. Commun., (1989) 320.

[0117] [16] D. F. Shriver M. A. Drezdzon, The manipulation of airsensitive compounds, pp 289-311, Wiley & Sons, Inc. (1986).

[0118] [17] M. I. Baraton, J. C. Labbe, P. Qiuintard, G. Roult, Mat Res. Bull., 20 (1985) 1239.

[0119] [18] http://ece-www.colorado.edu/˜bart/book/resistiv.xls

[0120] [19] D. K. Schroder, Semiconductor material and device characterization, Ch. 1. John Wiley & Sons, Inc. (1998).

[0121] [20] S. K. Dey, J. J. Lee, and P. Alluri, Jpn. J. Appl. Phys, 34 [6], 3142-3152 (1995).

[0122] [21] M. Houssa M. Naili, C. Zhao, H. Bender, M. M. Heyns and A. Stesmans, Semiconducto, Science and Technology, 16, 31-38 (2001).

[0123] [22] R. S. Johnson, G. Lucovsky, I. Baumvol, J. Vac. Sci. Technol., A19[4] 1353-1360 (2001).

[0124] [23] L. Lai, K. J. Herbert, and E. A. Irene, J Vac. Sci. Technol., B17 [1] 53-59 (1999). 

1. A compound having a formula XqYpZtO wherein X is silicon or carbon, Y is boron or nitrogen, Z is gallium or aluminum, O is oxygen and q and p are each an integer having a value of 1, 2 or 3 and t is zero or 1, provided that when X is silicon, and t is zero, Y is not nitrogen.
 2. Non-stoichiometric compounds of claim 1 wherein one or more of the values of q, p or t are non-integral. 3-5. (canceled)
 6. Compounds of claim 1 wherein X is Si and Y is boron.
 7. Compound of claim 3 having the formula Si₂B₂O.
 8. (canceled)
 9. Compounds of claim 1 wherein X is silicon and Y is nitrogen.
 10. Compounds of claim 1 wherein X is carbon and Y is boron.
 11. Compounds of claim 6 having the formula C₂B₂O. 12-59. (cancelled)
 60. A method of preparing disiloxane having the formula H₃SiOSiH₃ comprising the steps of contacting Cl₃SiOSiCI₃ with LiGaH₄ and capturing gaseous H₃SiOSiH₃ generated during the reaction. 61-62. (canceled)
 63. Thin film of Si₂N₂O made from disiloxane prepared by the method of claim
 8. 64. (canceled) 